THE EFFECT OF CARBON NANOFIBER TO A LIME-POZZOLANA CEMENT IN ORDER TO IMPROVE THE EARLY COMPRESSIVE STRENGTH OF THE CEMENT

IP.com Disclosure Number: IPCOM000234635D
Publication Date: 2014-Jan-23
Document File: 3 page(s) / 96K

Publishing Venue

The IP.com Prior Art Database

Abstract

This disclosure describes the effect of carbon nanofibers to a lime-pozzolana cement in order to improve the early compressive strength of the cement. The addition of carbon nanofibers to a traditional lime-pozzolana slurry resulted in a measureable fifty percent enhancement of the early compressive strength of the lime-pozzolana cement. Since early compressive strength is of critical importance to low temperature lime-pozzolana cement for use in well cementing applications, the additive of carbon nanofibers may hold a distinct value to lime-pozzolana formulations.

This text was extracted from a PDF file.
This is the abbreviated version, containing approximately 48% of the total text.

Page 01 of 3

THE EFFECT OF CARBON NANOFIBER TO A LIME‐POZZOLANA CEMENT IN ORDER TO IMPROVE  THE EARLY COMPRESSIVE STRENGTH OF THE CEMENT 

   

ABSTRACT   

This disclosure describes the effect of carbon nanofibers to a lime‐pozzolana cement in order to improve the early  compressive strength of the cement.   The addition of carbon nanofibers to a traditional lime‐pozzolana slurry resulted in  a measureable fifty percent enhancement of the early compressive strength of the lime‐pozzolana cement.  Since early  compressive strength is of critical importance to low temperature lime‐pozzolana cement for use in well cementing  applications, the additive of carbon nanofibers may hold a distinct value to lime‐pozzolana formulations. 

  THE INVENTION 

 


(1) Purpose of the Invention:  
 
This disclosure describes the effect of carbon nanofiber to a lime‐pozzolana cement in order to improve the early  compressive strength of the cement.   
 


(2) Description of the Invention:  
 

Core Description: 
 

Example 1 
 

The pozzolana‐lime cement composition is described as follows: 
  

The composition of the pumice suspension (liquid A1) for a 13.5 ppg slurry can be:           Mass    Concentration (bwoc)   

Water         300 g     Pumice          500 g    Lime (Ca(OH)2)        100 g  Liquiment 5581F (Polycarboxylated ether)    3.0 g   0.5%(bwoc)  MMCR (amino‐trismethylene phosphonic acid)    6.4 g   1.1% (bwoc) 
 
 

The composition of the pumice suspension (liquid A2) for a 13.5 ppg slurry can be:           Mass    Concentration (bwoc)   

Water         300 g     Pumice          500 g    Lime (Ca(OH)2)        100 g  Liquiment 5581F (Polycarboxylated ether)    3.0 g   0.5%(bwoc)  MMCR (amino‐trismethylene phosphonic acid)    6.4 g   1.1% (bwoc)  Carbon Nanofiber (Pyrograf)      1.2 g    0.2% (bwoc) 
 
These two slurries are retarded as decribed elsewhere such that it remains liquid under ambient conditions for an  extended period of time (from one month to over a year).   When the slurries are required for placement in well  cementing, a chemical activator is added to induce setting of the cement within a given pumping time for placement.      


Page 02 of 3

In order to increase the shelf life of the liquid slurry (prior to the addition of the accelerator) a powerful retarder is used.   The retarder used is (but not limited to) trisaminomethylene phosphonic acid or sodium amino‐trismethylene  phosphonate.   
 
Liquid B is then added as an accelerator to Liquid A1.  Separat...